Wuxi Zhongxin Special Steel Co.,Ltd.
Mission: to be the demonstrator of high quality development of steel industry and the leader of future steel industry
Add to Cart
Product Description
The main functions of steel (aluminum)-plastic composite tape in communication optical cable are shielding, anti-corrosion, waterproofing and strengthening, and it is one of the main auxiliary materials for communication optical cable. Stainless steel band.
| Characteristic | unit | value | Test Standard | |
| color | Natural/Blue | YD/T723-2007 | ||
| Thickness | Aluminium | 0.15/0.20 | mm | |
| Copolymer | 0.05 | mm | ||
| Tensile strength | MPa | ≥65 | ||
| Elongation | % | ≥15 | ||
| Peel strength | N/cm | ≥6.13 | ||
| Heat sealing strength | N/cm | ≥17.5 | ||
| The coefficient of kinetic friction | 矣 0.65 | |||
| Corrosion resistance | Grade | 7 | ||
| Filler Resistant Compounds and Hot Melt and Thixotropic Greases | not layered | |||
| water resistance,168hr, (68℃±1,168h) | N/cm | ≥6.13 | ||
| Dielectric Strength Both Sides | no breakdown | |||
| inside diameter | width | outer diameter | Core material |
| 76/150/406mm | 10mm-1000mm | Upto 1200mm | Cardboard/Steel/Plastic Core |
Main performance requirements of copolymers used in the production of composite tapes
1. Subject content and scope of application
It is suitable for copolymers for steel, copper and aluminum-plastic composite tapes, such as ethylene-acrylic acid copolymer, ethylene-methacrylic acid copolymer, etc.
2. Technical requirements
1. Appearance
The copolymer should be transparent or translucent particles, and the particle size should not be less than 30 particles per gram. Particles with black spots or impurities should not exceed 2%
2. Other performance requirements
| No. | Item | Performance requirements |
| 1 | density,h/cm3 | 0.930±0.005 |
| 2 | Melt Index,g/10min | 3.0~10.0 |
| 3 | Acrylic acid content or methacrylic acid content,% | ≥8.0 |
| 4 | melting point,℃ | 86~101 |
| 5 | Vicat softening point,℃ | ≥72 |
| 6 | tensile strength,MPa | ≥15 |
| 7 | Elongation at break,% | ≥400 |
| 8 | modulus,MPa | ≥60 |
3. Test method
1. Appearance
a Visual inspection of resin transparency and color;
b Particle size measurement - weigh 2g (accurate to 0.1g) of resin, count the number of particles, and calculate the particle size of the resin;
c Determination of particles with black spots - Weigh 50g (to 0.1g) of resin, pick out particles with black spots by visual inspection, weigh them, and calculate the percentage content.
Q: Would you provide samples For free?
A: Yes . with on stock specification We provide samples For Free . Freight charge collect